The high strength of rapid hardening cement at early stage, is due to its
Discussion:
56 comments Page 3 of 6.
Ghulam Nabi said:
6 years ago
All the difference of rapid hardening cement to that of ordinary portland cement is the quantity of lime stone (tri-calcium silicate) used as raw material, which gives the high early strength to the cement.
Rahul khan said:
6 years ago
Burning at high temperature and fine grinding gives more strength of cement.
MARI said:
6 years ago
Option D is correct. Because early strength (i.e) the first 7 days strength depends upon tricalcium silicate. But we have the only option to increase the calcium content by increase the lime cement.
Nitin said:
7 years ago
The heat of hydration increased by c3s content increased so early strength develop and if fineness of cement increases with an increase in strength.
Manisha Parajuli said:
7 years ago
It is option D.
SAGAR said:
7 years ago
Higher content of tricalcium silicate.
Ajeet said:
7 years ago
In RHC cement=finner grinding & high% of C3S &low% of C2S.
Hithesh said:
8 years ago
C3s, Only contribute hydration. Increased lime content helps to increase rapid hardening property.
Vishal said:
8 years ago
Option A is correct.
Viru kapoor said:
8 years ago
Yeah, It is due to finer grinding.