Initial setting of cement is caused due to
Discussion:
27 comments Page 2 of 3.
Amitkumarsachin said:
8 years ago
C3S is responsible to early strength not early setting time, C3A is responsiblefor early setting time.
Dharanidharan said:
6 years ago
Answer C is correct.
Be because.
C3s strenth property.
C3a time &hydration property.
Be because.
C3s strenth property.
C3a time &hydration property.
Aditya said:
6 years ago
The setting and hardenings of cement paste is mainly due to the hydration and hydrolysis.
PRITHVI said:
1 decade ago
Early gain of strength is caused due to tricalcium silicate and thus setting time too.
Meet said:
2 years ago
The flash setting of cement due to - C4AF,
Initial setting of cement due to - C3A.
Initial setting of cement due to - C3A.
(3)
Laxman prasad said:
8 years ago
How long time due to tri-calcium aluminate gains the initial setting by cement?
Basavaraj said:
7 years ago
C3S for initial setting.
C3A for the flash setting.
C2s for Ultimate strength.
C3A for the flash setting.
C2s for Ultimate strength.
ABHISHEK YADGIRI MUDIRAJ said:
7 years ago
C3S and C2S for strength and C3A for the early setting of cement.
Devaraj said:
9 years ago
Silica indicates strength aluminium indicates settings times.
Vikas said:
10 years ago
Tricalcium silicate responsible for early setting of cement.