Discussion Forum : Concrete Technology - Section 1 (Q.No. 39)
39.
The high strength of rapid hardening cement at early stage, is due to its
Discussion:
54 comments Page 5 of 6.
Jack said:
9 years ago
All the options are correct.
Reference M. S. Shetty.
Reference M. S. Shetty.
Manish bairagi said:
9 years ago
Early strength of RHC is mainly due to fine grinding and more content of C3S but for single purpose. What is the correct option b/w these two?
DARSHAN H A said:
9 years ago
Clearly given in books. The answer is both A and D.
Smily said:
10 years ago
Increase in lime content will increase the strength and hardening.
Galelio said:
10 years ago
@Anil Choudhary you are right.
Rapid hardening cement have increase fineness & c3s content.
Rapid hardening cement have increase fineness & c3s content.
Dimpi said:
10 years ago
First queries. What is lime cement? I am not aware about that kind of cement.
And answer should be fine grading or TriCalcium Silicate. But in question mentioned only "tricalcium".
Please give correct answer.
And answer should be fine grading or TriCalcium Silicate. But in question mentioned only "tricalcium".
Please give correct answer.
Mike said:
1 decade ago
RHC develops the strength rapidly at the age of 3 days, the same at that expected in opc in 7 days. The rapid rate development of strength is due to higher fine grinding and higher of C3S and lower of C2S, but I don't know how the answer is justified to Increase in lime content.
Nirav Bhatt said:
1 decade ago
All the options are participating in the high strength at early stage. To make RHC they are burnt at higher temperature and grinded fine.
Also increasing the lime content increases the amount of C3S. Hence all the options are correct. The answer is all of above.
Also increasing the lime content increases the amount of C3S. Hence all the options are correct. The answer is all of above.
(1)
Rajendran p said:
1 decade ago
Dear sir,
The early strength of RHC is achieved by the cement is grinding finer than the OPC. So surface area of cement will more and the finer cement will quick action with water and getting early strength. If adding more cement, cement will unsound.
The early strength of RHC is achieved by the cement is grinding finer than the OPC. So surface area of cement will more and the finer cement will quick action with water and getting early strength. If adding more cement, cement will unsound.
Soumya choudhury said:
1 decade ago
Its clearly written in books that the early strength of opc is due to fine grinding is responsible for its early strength. Also C3S is responsible for its early strength. So please, any body give the correct option.
(2)